Nanocrystalline diamond films deformation observed during sliding tests against Si3N4 balls as a possible cause for ripple formation on wear scars surface
Summary: Nanokristaliniu deimanto pleveliu šlyties deformacija, registruota saveikos su Si3N4 dalelemis bandymo metu, kaip galima nelygumu atsiradimo priežastis dilimo pavirušiuje, p. 480